TKES
Guaranteed Properties
Thickness
in (mm)
PowerCore Grade

Assumed Density
g/dm3

Core Loss W/kg at 1.5T at 50Hz

Magnetic Polarization (B) in Tesla

Anisotropy @
1.5 T
(in %)

No of bends
(Min)

@2500
(A/m)

@5000
(A/m)

@10000
(A/m)

0.35

35C235

7.60

2.35

1.49

1.60

1.70

± 17 %

2

35C250

7.60

2.50

1.49

1.60

1.70

± 17 %

2

35C270

7.65

2.70

1.49

1.60

1.70

± 17 %

3

35C300

7.65

3.00

1.49

1.60

1.70

± 17 %

3

35C330

7.65

3.30

1.49

1.60

1.70

± 17 %

3

0.50

50C250

7.60

2.50

1.49

1.60

1.70

± 17 %

2

50C270

7.60

2.70

1.49

1.60

1.70

± 17 %

2

50C290

7.60

2.90

1.49

1.60

1.70

± 17 %

2

50C310

7.65

3.10

1.49

1.60

1.70

± 14 %

3

50C330

7.65

3.30

1.49

1.60

1.70

± 14 %

3

50C350

7.70

3.50

1.50

1.60

1.70

± 12 %

5

50C400

7.75

4.00

1.53

1.63

1.73

± 12 %

5

50C470

7.75

4.70

1.54

1.64

1.74

± 10 %

10

50C530

7.75

5.30

1.56

1.65

1.75

± 10 %

10

50C600

7.75

6.00

1.57

1.66

1.76

± 10 %

10

50C630

7.75

6.30

1.55

1.65

1.76

± 10 %

10

50C700

7.80

7.00

1.60

1.69

1.77

± 10 %

10

50C800

7.80

8.00

1.60

1.70

1.78

± 10 %

10

0.65

65C330

7.60

3.30

1.49

1.60

1.70

± 15 %

2

65C350

7.60

3.50

1.49

1.60

1.70

± 14 %

2

65C400

7.65

4.00

1.52

1.62

1.72

± 14 %

2

65C470

7.65

4.70

1.53

1.63

1.73

± 12 %

5

65C530

7.70

5.30

1.54

1.64

1.74

± 12 %

5

65C600

7.75

6.00

1.56

1.66

1.76

± 10 %

10

65C700

7,75

7.00

1,57

1,67

1,76

± 10 %

10

65C800

7.80

8.00

1,60

1,70

1,78

± 10 %

10

65C1000

7.80

10.00

1,61

1,71

1,80

± 10 %

10

1.00

100C700

7.65

7.00

1.54

1.64

1.73

± 8 %

3

100C1000

7.80

10.00

1.58

1.68

1.76

± 6 %

10

100C1300

7.80

13.00

1.60

1.70

1.78

± 6 %

10

  • 1 For grades other than mentioned above please enquire separately.
    • 2 The specimens were tested as sheared
          • 3 Values were measured according to test method in IS 648 & IS649.

Typical Properties

Thickness
in (mm)
PowerCore Grade

Magnetic Properties

Physical Properties

Core Loss W/kg at 1.0T at 50Hz

Core Loss W/kg at 1.5T at 50Hz

Magnetic Polarization (B) in Tesla
'@5000
(A/m)

Vicker Hardness
HV1

YS
(N/mm2)

TS
(N/mm2)

% El
@ 80GL

0.35

35C235

0.95

2.30

1.61

220 ± 20

440 ± 30

530 ± 30

Min 8

35C250

1.00

2.45

1.63

220 ± 20

440 ± 30

530 ± 30

Min 8

35C270

1.10

2.60

1.63

220 ± 20

440 ± 30

530 ± 30

Min 8

35C300

1.15

2.85

1.63

200 ± 15

350 ± 30

480 ± 30

Min 10

35C330

1.25

3.15

1.63

180 ± 15

295 ± 30

445 ± 30

Min 18

0.50

50C250

1.00

2.45

1.61

220 ± 20

440 ± 30

530 ± 30

Min 8

50C270

1.10

2.60

1.63

220 ± 20

440 ± 30

530 ± 30

Min 8

50C290

1.12

2.75

1.63

220 ± 20

440 ± 30

530 ± 30

Min 10

50C310

1.20

2.95

1.63

200 ± 20

350 ± 30

480 ± 30

Min 10

50C330

1.30

3.15

1.64

180 ± 15

295 ± 30

445 ± 30

Min 18

50C350

1.45

3.35

1.64

180 ± 15

295 ± 30

445 ± 30

Min 18

50C400

1.60

3.85

1.64

155 ± 15

250 ± 30

380 ± 30

Min 20

50C470

1.90

4.20

1.66

155 ± 15

250 ± 30

380 ± 30

Min 30

50C530

2.15

4.70

1.67

155 ± 15

250 ± 30

380 ± 30

Min 30

50C600

2.50

5.40

1.67

155 ± 15

250 ± 30

380 ± 30

Min 30

50C630

2.50

5.50

1.70

145 ± 15

260 ± 30

385 ± 30

Min 30

50C700

2.70

6.00

1.70

145 ± 15

260 ± 30

385 ± 30

Min 30

50C800

2.80

6.50

1.71

145 ± 15

260 ± 30

385 ± 30

Min 30

0.65

65C330

1.30

3.15

1.62

220 ± 20

440 ± 30

530 ± 30

Min 8

65C350

1.45

3.35

1.63

220 ± 20

440 ± 30

530 ± 30

Min 8

65C400

1.70

3.85

1.63

190 ± 15

320 ± 30

445 ± 30

Min 18

65C470

1.90

4.30

1.64

155 ± 15

250 ± 30

380 ± 30

Min 20

65C530

2.15

4.70

1.65

155 ± 15

250 ± 30

380 ± 30

Min 20

65C600

2.50

5.50

1.67

155 ± 15

250 ± 30

380 ± 30

Min 30

65C700

2.90

6.00

1.68

145 ± 15

260 ± 30

385 ± 30

Min 30

65C800

3,10

6.80

1.70

145 ± 15

260 ± 30

385 ± 30

Min 30

65C1000

4.30

8.00

1.72

130 ± 15

235 ± 30

350 ± 30

Min 30

1.00

100C700

3.00

6.50

1.65

180 ±15

295 ± 30

445 ± 30

Min 18

100C1000

4.30

9.00

1.69

155 ± 15

250 ± 30

380 ± 30

Min 30

100C1300

5.50

12.00

1.71

155 ± 15

250 ± 30

380 ± 30

Min 30

  • 1 For grades other than mentioned above please enquire separately.
    • 2 The specimens were tested as sheared
          • 3 Values were measured according to test method in IS 648 & IS649.
          • 4 For any further detail please contact nearby sales office.